Building components- floor towards attic (uninhabitable) - ddrtxn04b
 
 


Cross-section of standard configuration
[Additional views]

Last update08.09.2014/hfa.plb
floor towards attic (uninhabitable): timber frame construction, not suspended, dry

register of building materials used for this application, cross-section
(from top to bottom, dimensions in mm)

  Thickness Building material  λ   μ min - max   ρ   c  Reaction to fire
EN
 50.0 Magnesite-bound lightweight wood wool board   0,120  2 - 5  700  1,400   
 24.0 spruce wood cladding with spacing of cladding boards(24/100); a=400  0,130  50  500  1,600   D
*   finger-jointed solid construction timber (80/..; e=*)  0,130  50  500  1,600   D
*   Insulation material            
  vapour barrier sd≥ 2m       1000     
 24.0 spruce wood cladding with spacing of cladding boards(24/100); a=400  0,130  50  500  1,600   D
 25.0 gypsum plasterboards with improved properties at high temperatures (fire) (2x12,5 mm) or  0,250  10  800  1,050   A2
 25.0 gypsum fibre board (2x12,5 mm)  0,320  21  1000  1,100   A2
   
               
  Variations of building components

No. Thickness of layer Note Fire performance Thermal performance Acoustic performance Eco Sustainability Mass HTMLPDF
  C* D* Σ   REI U [W/(m²K)] mw,B,A [kg/m²] Diffusion Ln,w(Cl) Rw(C,Ctr) OI3Kon m [kg/m²]   
00   220  220  343,0  e=625
 
60  0,18  26,1  adequate  –  44(-2,-6)  -5,5  76,4   ddrtxn04b-00  
E = glass wool [0,0040; R=16]
01   200  200  323,0  e=625
 
60  0,20  26,1  adequate  –  43(-1,-5)  -6,7  74,9   ddrtxn04b-01  
E = glass wool [0,0040; R=16]
02   240  240  373,0  e=625
 
60  0,17  26,1  adequate  –  44(-1,-5)  -4,3  78,0   ddrtxn04b-02  
E = glass wool [0,0040; R=16]
03   220  220  343,0  e=625
 
60  0,17  26,1  adequate  –  44(-1,-5)  -5,5  82,9   ddrtxn04b-03  
E = glass wool [0,0035; R=50]
04   220  220  343,0  e=625
 
60  0,18  26,1  adequate  –  43(-1,-5)  -2,8  79,7   ddrtxn04b-04  
E = mineral wool [0,038; R=33]
05   220  220  343,0  e=625
 
60  0,18  26,1  adequate  –  44(-2,-6)  -14,7  83,9   ddrtxn04b-05  
E = cellulose fibre [040; E]
06   220  220  343,0  e=625
 
60  0,20  26,1  adequate  –  43(-3,-7)  -14,1  76,4   ddrtxn04b-06  
E = sheep wool [0,041; R=16]
07   220  220  343,0  e=400
 
60  0,20  27,2  adequate  –  40(-3,-7)  -6,1  84,1   ddrtxn04b-07  
E = glass wool [0,0040; R=16]